The data was acquired by scanning Hall microscopy (SHM) in the rapid 'flying' mode that makes a rapid 2D magnetic scan of the maximum field of view. The data files consist of individual SHM images collected during these scans along with the appropriate text files for their averages.
B-H loops were measured via the SHPM in fields up to 107mT and 3.2mT.

Transport data was performed in an Oxford Instruments Cryostat cooled by liquid Nitrogen. A current of 10mA was supplied while the voltage was measured using a Keithley 182 nanovoltmeter as the temperature was swept at 0.1K/min using an OI ITC 503 temperature controller.

Field Effect Scanning Electron Microscopy (FE-SEM) at 5kV and 1kV and Energy Dispersive X-Ray Analysis (EDX) at 10kV were performed in a Joel JSM-6301F FE-SEM.